High Hardness Microcrystal Alumina Lining Brick
Product Series:BM92/BMG95/BME95
Product Material:Alumina ceramic
Alumina Content: 92% 95%
Product Color:White
Product Size: Customized
Introduction
High Hardness Microcrystal Alumina Lining Brick can be used for glaze and ceramic tile body grinding. The product has the characteristics of high hardness, high density, low abrasion, good regularity, and corrosion resistance. It is used for wear-resistant lining of ball mills and is widely used in ceramics, cement, paint, pigments, chemicals, medicine, coatings, inorganic mineral powders, etc. It can effectively improve the grinding efficiency, reduce the grinding cost and reduce product pollution.
Properties
High-quality alumina powder is used as raw material, thus has high purity and greatly reduces the pollution caused by grinding
materials.
Our High Hardness Microcrystal Alumina Lining Brick has good wear resistance, the wear resistance is 266 times that of manganese steel, effectively prolonging the service life of equipment;
Matched with our own alumina grinding balls, the slurry is fine, corrosion-resistant, high-density, and high-mechanical strength.
Application Field
High Hardness Microcrystal Alumina Lining Brick is widely used in the lining of ball mills in industries such as ceramics, paint, pigment, chemical industry, medicine, coating, inorganic mineral powder, etc.
Why choose High Hardness Microcrystal Alumina Lining Brick?
Firstly, its microcrystalline structure provides excellent mechanical strength, wear resistance, and thermal shock resistance, making it suitable for use in high-temperature and high-wear environments.
Secondly, its high hardness property ensures good abrasion resistance, preventing damage to the equipment and reducing maintenance costs.
Finally, it is easy to install and maintain, providing a cost-effective solution for improving the performance and lifespan of industrial equipment.
Specification
|
Series |
BM92 |
BMG95 |
BME95 |
|
AL2O3 (%) |
92±0.5 |
95±0.5 |
95±0.5 |
|
ZrO2 (%) |
- |
- |
- |
|
Bulk density(g/cm3) |
≥3.6 |
≥3.65 |
≥3.7 |
|
Compressive strength (MPa) |
≥1050 |
≥1300 |
≥1600 |
|
Bending strength (MPa) |
≥220 |
≥250 |
≥300 |
|
Fracture toughness (MPam1/2) |
≥3.70 |
≥3.80 |
≥4.0 |
|
Rockwell hardness (HRA) |
≥82 |
≥85 |
≥88 |
|
Loss bulk (cm3) |
≤0.25 |
≤0.2 |
≤0.15 |
About us
Hot Tags: high hardness microcrystal alumina lining brick, manufacturers, suppliers, factory, price, made in China, Wear Resistant Ceramic Composite Plates, Industrial Ceramic Alumina Tiles, alumina ceramic adhesive, Abrasion Resistance Ovelay Plate, resistance of alumina ceramic, alumina ceramic lining brick