Product Name:Chute Liner Plates
Product Material:Alumina Ceramic
AL2O3 Content(%):92/95
Product Color:White
Bulk density(g/cm3):≥3.6/≥3.7
Hardness(Mohs):9

Send Inquiry

Product Introduction

Product Introduction

Chute liner plates is a wear-resistant ceramic material that can be used in high temperature and high pressure environments. It is made of high-purity alumina material through a special process. Alumina ceramic materials have the characteristics of high hardness, corrosion resistance and oxidation resistance. Due to these properties, alumina ceramic lining plates are widely used in casting, metallurgy, glass, cement, chemical industry and other fields.

Characteristic

1. Good corrosion resistance: Alumina ceramic materials have strong corrosion resistance and can function stably in various corrosive media environments such as acids, alkalis, and salts for a long time.
2. High purity: Alumina ceramic materials have high purity and do not contain impurities such as metal impurities. They are suitable for the chemical industry and metal metallurgy industry.
3. Easy installation: Chute liner plates is made of lightweight materials and is easy to install.

Application

Chute liner plates are widely used in casting, metallurgy, glass, cement, chemical industry and other fields. Specific application scenarios include the following aspects.
1. Foundry industry: In the foundry industry, in order to ensure the stability of the equipment and extend the service life of the equipment, chute linings are usually used in casting equipment and melting equipment.
2. Metallurgical industry: In the metallurgical industry,this arc liners are usually used for high temperature and high pressure furnace lining plates and chemical reactor lining plates. According to its high temperature wear resistance, corrosion resistance and other characteristics, it can meet the following conditions: the needs of high temperature and high pressure furnace lining plates and chemical reactor lining plates.
3. Glass industry: In the glass industry, chute liner plates are usually used as glass furnace linings. Because the melting of glass requires a high-temperature and high-pressure environment, alumina lining with high temperature wear resistance and corrosion resistance is required. Alumina liners are suitable to meet this requirement.

Specification

Series	BM92	BMG95	BME95	BMZTA	BMZR
AL2O3(%)	92±0.5	95±0.5	95±0.5	≥75	-
ZrO2(%)	-	-	-	≥21	94.8±0.5
Bending strength (Mpa)	≥220	≥250	≥300	≥400	≥800
Compressive strength (Mpa)	≥1050	≥1300	≥1600	≥2000	-
Fracture toughness (MPam1/2)	≥3.70	≥3.80	≥4.0	≥4.5	≥7
Rockwell hardness (HRA)	≥82	≥85	≥88	≥90	≥88
Wear volume(cm3)	≤0.25	≤0.2	≤0.15	≤0.05	≤0.02
Bulk density(g/cm3)	≥3.6	≥3.65	≥3.7	≥4.1	≥5.9