Product Name:White Hexagon Tile
Product Material:Alumina Ceramic
AL2O3 Content(%):92/95
Product Color:White
Bulk density(g/cm3):≥3.6/≥3.7
Hardness(Mohs):9

Send Inquiry

Product Introduction

Product Introduction

White hexagonal tiles are available in a variety of shapes and forms.The most common shape is the regular hexagon, which has six equal sides and angles.Tiles can be produced in different sizes.The thickness of the tiles may also vary, depending on the intended application.

Characteristic

White hexagonal tiles mainly have the following advantages:

1. High hardness: The hardness of wear-resistant white hexagonal tiles is higher than ordinary steel and cast iron.It has a Rockwell hardness of more than 80HRA.
2. Good wear resistance: The surface of wear-resistant white hexagonal tiles has been sintered and extruded at high temperature and has good wear resistance,its loss buck is small and not easy to change its shape.At the same time,it is friendly to machinery.
3. Corrosion resistance: Wear-resistant White hexagonal tiles have excellent acidic and alkaline corrosion properties.

4.Good safety: hexagonal wear-resistant Mosaic industrial ceramics are not radioactive, will not cause pollution and harm to the environment.

Application

White hexagonal tiles is a unique and versatile material.Due to its excellent performance, durability and aesthetics, it is widely used in various industries.Such as steel, cement, coal, ports and other industries.With its excellent performance and diverse applications,hexagonal alumina tiles are expected to play an increasingly important role in the development of modern technology.

If you have any questions, please feel free to contact us, welcome to inquire!

Specification

Series	BM92	BMG95	BME95	BMZTA	BMZR
AL2O3(%)	92±0.5	95±0.5	95±0.5	≥75	-
ZrO2(%)	-	-	-	≥21	94.8±0.5
Bending strength (Mpa)	≥220	≥250	≥300	≥400	≥800
Compressive strength (Mpa)	≥1050	≥1300	≥1600	≥2000	-
Fracture toughness (MPam1/2)	≥3.70	≥3.80	≥4.0	≥4.5	≥7
Rockwell hardness (HRA)	≥82	≥85	≥88	≥90	≥88
Wear volume(cm3)	≤0.25	≤0.2	≤0.15	≤0.05	≤0.02
Bulk density(g/cm3)	≥3.6	≥3.65	≥3.7	≥4.1	≥5.9