Product Name:Weldable Ceramic Tile
Product Material:Alumina Ceramic
AL2O3 Content(%):92/95
Product Color:White
Bulk density(g/cm3):≥3.6/≥3.7
Hardness(Mohs):9

Send Inquiry

Product Introduction

Product Introduction

Weldable ceramic tiles are made by mixing alumina raw materials and forming a flowing material through a series of forming, processing, sintering and finishing processes under high temperature and high pressure conditions. During the sintering process, alumina raw materials are typically stuffed into the porcelain. Porous media is added to the plate mold, and an weldable ceramic tile is made through shaping and sintering processes. The manufacturing and processing processes are complex and require professional and technical personnel from the manufacturer to operate them.

Characteristic

Weldable ceramic tile is a very high-quality high-temperature material with excellent heat resistance and high-temperature strength. It also has the advantages of low resistance, easy maintenance, high mechanical strength, It can increase productivity, reduce production disruptions, and provide a safer working environment.

Application

1. Lining plates for cement product manufacturing equipment in the construction field;
2. Conveying pipelines for fly ash, ash and other materials, and lining boards for storage equipment.
3. Lining plates for blast furnaces, hot air heaters and other high-temperature equipment in steel companies.

Maintenance

The following principles should be followed during the use of weldable ceramic tile.
1. Avoid direct impact or collision: During operation or transportation, direct impact or collision between mechanical devices or other hard objects and the liner should be avoided.
2. Please avoid bending and deformation. During use, please avoid bending and deformation of the alumina orifice plate liner. Otherwise, service life and performance will be affected.
3. Regular inspection: Regularly check the surface condition of the gasket and replace or repair damaged parts in time if necessary.

Specification

Series	BM92	BMG95	BME95	BMZTA	BMZR
AL2O3(%)	92±0.5	95±0.5	95±0.5	≥75	-
ZrO2(%)	-	-	-	≥21	94.8±0.5
Bending strength (Mpa)	≥220	≥250	≥300	≥400	≥800
Compressive strength (Mpa)	≥1050	≥1300	≥1600	≥2000	-
Fracture toughness (MPam1/2)	≥3.70	≥3.80	≥4.0	≥4.5	≥7
Rockwell hardness (HRA)	≥82	≥85	≥88	≥90	≥88
Wear volume(cm3)	≤0.25	≤0.2	≤0.15	≤0.05	≤0.02
Bulk density(g/cm3)	≥3.6	≥3.65	≥3.7	≥4.1	≥5.9