Product Name:Bent Liner
Product Material:Alumina Ceramic
AL2O3 Content(%):92/95
Product Color:White
Bulk density(g/cm3):≥3.6/≥3.7
Hardness(Mohs):9

Send Inquiry

Product Introduction

Product Introduction

Bent liner is a kind of high-tech ceramic product made of high purity alumina material.It has strong wear resistance, corrosion resistance, high temperature resistance and other excellent properties.It can be used as equipment lining under various working conditions such as high temperature, high pressure and corrosion.

Properties

1. Good wear resistance: Alumina ceramic bent liners have high hardness, their wear resistance is more than 7 times that of steel, and their wear resistance is very good.
2. Good corrosion resistance: Alumina ceramic bent liners have good corrosion resistance and can withstand corrosion from corrosive media such as acids, alkalis, and salts for a long time, and have a long service life.
3. Good high temperature resistance: Alumina ceramic bent liners have good high temperature resistance and can be used stably for a long time in high temperature environments.
4. High density: Alumina ceramic curved plates have high density, up to 3.7g/cm3 or more, and have excellent compressive strength.

Applications

Alumina ceramic bent liner is mainly used for equipment lining under harsh working conditions such as high temperature, high pressure, corrosion, etc. Common application equipment are: dry mill,high temperature furnace, electric arc furnace, rotary kiln, filter,absorber, kiln,steam boiler,converter, cement kiln,sewage filter, etc.

In the above equipment, because the alumina ceramic bent liner has good wear resistance, corrosion resistance, high temperature resistance and other excellent properties, it can effectively protect the inside of the equipment from damage, extend the service life of the equipment, and improve the output efficiency.

Specification

Series	BM92	BMG95	BME95	BMZTA	BMZR
AL2O3(%)	92±0.5	95±0.5	95±0.5	≥75	-
ZrO2(%)	-	-	-	≥21	94.8±0.5
Bending strength (Mpa)	≥220	≥250	≥300	≥400	≥800
Compressive strength (Mpa)	≥1050	≥1300	≥1600	≥2000	-
Fracture toughness (MPam1/2)	≥3.70	≥3.80	≥4.0	≥4.5	≥7
Rockwell hardness (HRA)	≥82	≥85	≥88	≥90	≥88
Wear volume(cm3)	≤0.25	≤0.2	≤0.15	≤0.05	≤0.02
Bulk density(g/cm3)	≥3.6	≥3.65	≥3.7	≥4.1	≥5.9