Zirconia Ceramic Beads
Product Material: zirconia
ZrO2(%) : 95
Y2O3(%) : 5
Mohs Hardness : 9
Real density(g/cm3) : >=6.0
Bulk density(g/cm3) : 3.65
Self wearing rate :2ppm
color :white
package: 25kg/barrel
Size : dia0.1-50mm
Product details
Zirconia ceramic beads are made of zirconia and other stabilizers (such as yttrium oxide) by rolling into balls/press molding/dropping into balls, and are more wear-resistant than alumina balls and steel balls.
The production process of zirconia beads includes powdering, forming, sintering, polishing, sieving and other processes.
Advantage
Zirconia ceramic beads have the characteristic of high strength, suitable for sand mills with high linear speed, will not break during high-speed operation, and at the same time, the grinding loss is very small, it can be said that there is almost no self-wear, and yttrium-stabilized zirconia beads have become the mainstream choice. Yttrium stabilized zirconia beads are very popular in the grinding industry.
The standards
The requirements for grinding zirconium beads are actually similar across many application fields, including the coating industry, such as medicine, cosmetics, and agrochemicals, such as: precise composition ratio, large specific gravity, high grinding efficiency and low wear of grinding zirconium beads, good stability, while ensuring low crushing rate. The less probable it is to shatter, the stronger the strength and hardness of the ground zirconium beads. Additionally, ingredients must be ensured.
Application
Digital inkjet ink: thermal transfer ink, solvent ink, eco-solvent ink, digital printing paint ink, digital printing disperse dye ink, pigment ink, LED-UV special curing ink, water-based universal pigment ink, coating ink, printing ink, Pen ink.
Parameter
Series | BMYG95 |
ZrO2 (%) | 95±0.5 |
Y2O3 (%) | 5 |
Hardness (Mohs) | 9 |
Real density (g/cm3) | ≥6.0 |
Bulk density (g/cm3) | 3.65 |
Self wearing rate (%) | 2ppm |
Available size (mm) | 0.1mm 0.2mm 0.3mm 0.4-0.6mm 0.6-0.8mm 0.8-1.0mm 1.0-1.2mm 1.2-1.4mm 1.4-1.6mm 1.8-2.0mm 2.0-2.2mm 2.2-2.4mm 2.4-2.6mm 2.6-2.8mm 2.8-3.0mm 3.0-3.2mm 3.2-3.4mm 3.6-3.8mm 4mm 5mm 8mm 10mm 15mm 20mm 25mm 30mm 40mm 50mm |
Picture
Our other grinding media ball
The production process
FAQ
We are based in Shandong province, China, professional in wear-resistant ceramic ,sell goods to everywhere of the world.
2. How can we guarantee quality?
Always a pre-production sample before mass production;
Always regular quality inspection during mass production
Always final Inspection before shipment;
7-20days working days after all information is confirmed (according to different products).
Send your message to our sales staff in the input box below and we will get back to you within a few hours on business days.
Hot Tags: zirconia ceramic beads, manufacturers, suppliers, factory, price, made in China, alumina grinding media, Zirconia Balls, alumina toughened zirconia, Zirconia Beads, Zirconia Toughened Alumina Balls, Zirconia Toughened Alumina Beads
Previous
Yttrium ZirconiaYou Might Also Like
Send Inquiry